Nd: YAG laser for debonding ceramic orthodontic brackets.

Hayakawa K

Department of Orthodontics, Tokyo Dental College, Masago, Chiba, Japan. kota@eruna.net

INTRODUCTION: The purpose of this study was to develop an effective method for debonding ceramic orthodontic brackets with a high-peak power Nd:YAG laser. METHODS: Two types of ceramic brackets (single crystal and polycrystalline) were bonded to mandibular bovine teeth with 2 types of bonding resins (4-META/MMA and Bis-GMA). The laser was applied to 2 points on each bracket, each with a 1-pulse-per-second shot. Bond strength and thermal effects of the laser on the dentin surface were assessed at 3 laser energy levels: 1.0, 2.0, and 3.0 joules (J). Shear tests were performed on the irradiated test group and on a nonirradiated control group. ANOVA was used to determine significant differences. RESULTS: The shear test (P < .05) showed that every specimen in the 2.0-J and 3.0-J groups underwent a significant decrease in bonding strength compared with the nonirradiated group. However, the 1.0-J group did not exhibit any such difference. In the 2 former groups, laser irradiation alone was sufficient to debond some specimens. No significant difference was found between bonding resins. The maximum temperature rise measured on the pulpal walls at the lasing points was 5.1 degrees C. CONCLUSIONS: The application of a high-peak power Nd:YAG laser at 2.0 J or more is effective for debonding ceramic brackets.

Published 15 November 2005 in Am J Orthod Dentofacial Orthop, 128(5): 638-47.
Full-text of this article is available online (may require subscription).

© 2005-2008 Orthodontic Research Today. All Rights Reserved.